Cr12Mo1V1淬火及回火后斷裂,斷口为朽木狀,請教各位前輩!

w1111111

<font size="3"><font face="新細明體">&nbsp;<stroke joinstyle="miter"></stroke></font></font><formulas><f eqn="if lineDrawn pixelLineWidth 0"></f><f eqn="sum @0 1 0"></f><f eqn="sum 0 0 @1"></f><f eqn="prod @2 1 2"></f><f eqn="prod @3 21600 pixelWidth"></f><f eqn="prod @3 21600 pixelHeight"></f><f eqn="sum @0 0 1"></f><f eqn="prod @6 1 2"></f><f eqn="prod @7 21600 pixelWidth"></f><f eqn="sum @8 21600 0"></f><f eqn="prod @7 21600 pixelHeight"></f><f eqn="sum @10 21600 0"></f></formulas><path gradientshapeok="t"></path><lock aspectratio="t" vext="edit"></lock><shape id="_x0000_s1026" type="#_x0000_t75" style="MARGIN-TOP: 75.85pt; Z-INDEX: 1; MARGIN-LEFT: 53.7pt; WIDTH: 489.6pt; POSITION: absolute; HEIGHT: 348.5pt; mso-position-horizontal-relative: page; mso-position-vertical-relative: page;"><imagedata otitle="IncaTemp0" src="file:///C:\DOCUME~1\F2704111\LOCALS~1\Temp\msohtml1\01\clip_image001.png"></imagedata><wrap anchory="page" anchorx="page"></wrap></shape>

zhengli

<p>kan bu dao!</p>

w1111111

<p>2樓兄弟,留個地址交流一下吧</p><p><a href="mailto:gliangwang@tom.co">gliangwang@tom.co</a>m</p>

半片叶

<p>我怀疑 不是淬火的问题，而是磨的问题。</p><p>我们的一个客户就一直出现那样的问题，我看过了，</p><p>材料没有问题，热处理没有问题，只是磨的问题，</p><p>在磨的时候一次进刀量太大了，导致局部发热严重***********</p><p>******</p>

chenjunjun

学习中，呵呵[em01]

成刚钢材

<p>看不见，请楼主修改一下。</p><p>PS：我不知怎么弄。</p>

longyanjiu

浮躁的人容易问：我到底该学什么_别问，学就对了；
浮躁的人容易问学proe有钱途吗_建议你去抢银行；
浮躁的人容易说:我要中文版！我英文不行_不行？学呀；
只观望而不学的人和只学而不坚持的人永远不是一个高手

wenrong

我看不到，估计是过硬啊，D2是1010度，15秒，后取出来空气冷却，60以上100以下，再进去低温回火

hsq1963

先化验一下材质,我们用D2(国产)有10多年的历史,没有发现这个问题