[讨论]关于折弯的一道问题

heart112

<p>工件相关图片如下:</p><p></p><p>工件图纸只是随手画画,但实际生产中的工件结构是类似.还有一些是整个工件有成排的压胫.</p><p>诸如此类的折弯,在工件的弯角处,极为容易产生皱折.如果只是简单地设计为直接折弯,将不可避免地产生皱折,而且随着胫的高度越高,皱折越大.就我这图纸的工件,产生的皱折收缩长宽将进50mm,深近10mm.</p><p>想过尝试在凹凸的弯角处加入弹性胶,以增强工件受夹紧力,但估计对料厚小、胫高度矮的有点用处。如图工件则无多少效果。</p><p>不知各位高手可有什么好的解决方法？<br/><br/></p>

heart112

失望!诺大一个论坛,还说有很多高手!都没人能做得出来.

gogososo

<p>没办法!!</p><p></p>

cslelch1

<p>起皱是由于转角处材料太多无法吸收的原故，改下展开吧。</p>

zhwl

你做的展开图有问题，

LIAOYAO

<span style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: 細明體; mso-ascii-font-family: &#718;&#805;; mso-hansi-font-family: &#718;&#805;; mso-fareast-language: ZH-TW; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;"><font size="5"><span lang="ZH-CN" style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: SimSun; mso-ascii-font-family: &#718;&#805;; mso-hansi-font-family: &#718;&#805;; mso-fareast-language: ZH-CN; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;">改变工法可以避免皱折，先弯再成形</span><span lang="EN-US" style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: &#718;&#805;; mso-fareast-language: ZH-CN; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-fareast-font-family: SimSun; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;"><font face="新細明體">(</font></span><span lang="ZH-CN" style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: SimSun; mso-ascii-font-family: &#718;&#805;; mso-hansi-font-family: &#718;&#805;; mso-fareast-language: ZH-CN; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;">会有破裂情况喔</span><span lang="EN-US" style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: &#718;&#805;; mso-fareast-language: ZH-CN; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-fareast-font-family: SimSun; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;"><font face="新細明體">)</font></span><span lang="ZH-CN" style="FONT-SIZE: 9pt; COLOR: #000003; FONT-FAMILY: SimSun; mso-ascii-font-family: &#718;&#805;; mso-hansi-font-family: &#718;&#805;; mso-fareast-language: ZH-CN; mso-bidi-font-family: &quot;Times New Roman&quot;; mso-font-kerning: 1.0pt; mso-ansi-language: EN-US; mso-bidi-language: AR-SA;">。</span></font></span>

ddw200099

<p>高手也不会说给你听，这种态度，我不是高手，hehe</p><p>我没做过这种模具，想法是加热该产品，在凸凹模都为转轴模的模里折弯，相对滑动较大，回擦伤，所以转轴中心位置要计算，使折弯前后材料相对模具滑动最少，高手</p><p>看你这东西也不是什么精密的东西，还高手</p>

leevesun

<p>可以考虑在管中灌沙，考虑到你的态度问题，我能说的就这些，顺便说一句，我也不是高手，供参考。</p>

STAR123

<p>我们厂里经常折弯方管之类的,估计你的R太下了,</p><p>这么小很难折的,</p><p>如果是圆管,你去观察下,他里面是缩小内凹的,</p><p>=========================================</p><p>可以考虑用专用的折弯设备,应该能解决的问题</p>

FANZAI

<div class="msgheader">QUOTE:</div><div class="msgborder"><b>以下是引用<i>heart112</i>在2006-3-12 15:19:00的发言：</b><br/>失望!诺大一个论坛,还说有很多高手!都没人能做得出来.</div><p>这样说话不好吧!</p>